Description

025

037

050

100

150

250

Wire diameter (micro m)

25

37

50

100

150

250

Min bend radius (mm)

1.3

1.8

2.5

5

7.5

12.5

Linear resistance (ohm/m)

1770

860

510

150

50

20

Recommended current (mA) [1]

20

30

50

180

400

1000

Recommended power (W/m) [1]

0.71

0.77

1.28

4.86

8

20

Max. recovery force (N) [2]

0.284

0.645

1.147

4.599

10.356

28.763

Rec. recovery force (N) [3]

0.069

0.204

0.343

1.471

3.236

9.12

Rec. deformation force (N) [4]

0.02

0.039

0.078

0.275

0.608

1.687

Min. contraction time (sec)

0.1

0.1

0.1

0.1

0.1

0.1

Relaxation time (sec)

0.1

-

0.3

0.8

2

5.5

Typical cycle rate (cycles/min)

55

52

46

33

20

9

General Properties

Activation start temperature

68°C

Activation finish temperature

78°C

Effective transition temperature

70°C

Relaxation start temperature

52°C

Relaxation finish temperature

42°C

Annealing temperature

540°C

Melting temperature

1300°C

Heat capacity

0.322J/g°C

Latent heat

242J/g

Density

645g/cc

Energy conversion efficiency

5%

Max. deformation ratio

8%

Recommended deformation ratio

3 - 5%

Youngs Modulus

28GPa